BENTONITE RHEOLOGY MODIFIER HY-70W-1

Product introduction:

HY-70W-1 is a synthetic lithium magnesium silicate.It is not soluble in water but it can expand with water to form a colorless transparent colloid.High thixotropic colloids can be formed when the concentration in water is more than 2%.

 

Physicochemical indexes

Appearance

White powder

Moisture content(105℃)

≤10.0%

Particle size(Through 200mesh)

≥95%

Viscosity (2%clay,98% water),cps

≥1500mpa.s

Density

2.3～2.6g/cm3

PH value(2%clay,98% water)

9～11

Transparency(2%clay,98% water)

≥70



Physical and chemical indicators
usage method
application
Packaging, storage and transportation
外观 白色粉末
烧失量
细度， 目)
水份 ≤10
粘度 ≥1500 mpa.s
Appearaance White powder
Loss in ignition
Fineness， mesh)
Moisture content ≤10
Viscosity ≥1500 mpa.s
The 70W-1 series synthetic inorganic gel needs to prepare a pre-gel before use. After adding it to water and stirring evenly, let it stand for more than 15 hours to fully expand the product and form a gel. This process can be accelerated in hot water.
It has excellent thixotropy in various aqueous formulation systems. These formulations can be applied to products for household and industrial surface coatings, cleaners, ceramic glazes, agriculture, oil fields, forestry, aquaculture and horticulture. The sol-pre-gel system formed by the HY-70W-1 series products can be used as a thixotropic agent, anti-sagging agent and anti-settling agent for waterborne coatings.
HY-70W-1 is hygroscopic and should be stored in a dry environment.